Product Introduction：
Radiation-crosslinkable low-fluorine-emission ethylene-tetrafluoroethylene copolymer is a low-fluoride-emission fluorine material with excellent comprehensive mechanical properties, electrical properties, and chemical resistance. After irradiation modification, a thermosetting material with a three-dimensional network structure is formed, thereby further improving the temperature resistance, cutting resistance, mechanical strength, and service life of the material. The product has the following characteristics:
1.Low fluoride emission, less corrosion to electronic equipment, suitable for airtight or vacuum installation occasions;
2.Wide temperature range, after crosslinking -60℃~200℃
3.Excellent chemical resistance;
4. Flame retardant; High strength;
5.Suitable for thin-wall extruded cables and weight-reducing occasions;
Application fields：
Radiation-crosslinkable low-fluorine-emission ethylene-tetrafluoroethylene copolymer has excellent processing properties and is very suitable for extrusion into various products such as cables, pipes, injection molded parts, heating elements, etc., after being irradiated by an electron accelerator The performance is further improved, making its performance more stable and reliable. Widely used in fields that require high temperature resistance, chemical resistance, flame retardancy, and weather resistance, such as aerospace cables, heat-shrinkable sleeves for electronic appliances, architectural films, heating cables in chemical plants, oil field detection cables, satellite cables, and electric tools cables etc.
Product performance index:
Product 产品 | Density 密度g/cm3 | Melting point熔点 ℃ | 拉伸强度MPa | 断裂伸长率 % | Fluoride escape is 1ppm 氟化物逸出量1ppm | 加工温度 ℃ |
TS-4150LF | 1.75 | 260 | 35~45 | 15~250 | <40 | 260~320 |
Product Introduction：
Radiation-crosslinkable low-fluorine-emission ethylene-tetrafluoroethylene copolymer is a low-fluoride-emission fluorine material with excellent comprehensive mechanical properties, electrical properties, and chemical resistance. After irradiation modification, a thermosetting material with a three-dimensional network structure is formed, thereby further improving the temperature resistance, cutting resistance, mechanical strength, and service life of the material. The product has the following characteristics:
1.Low fluoride emission, less corrosion to electronic equipment, suitable for airtight or vacuum installation occasions;
2.Wide temperature range, after crosslinking -60℃~200℃
3.Excellent chemical resistance;
4. Flame retardant; High strength;
5.Suitable for thin-wall extruded cables and weight-reducing occasions;
Application fields：
Radiation-crosslinkable low-fluorine-emission ethylene-tetrafluoroethylene copolymer has excellent processing properties and is very suitable for extrusion into various products such as cables, pipes, injection molded parts, heating elements, etc., after being irradiated by an electron accelerator The performance is further improved, making its performance more stable and reliable. Widely used in fields that require high temperature resistance, chemical resistance, flame retardancy, and weather resistance, such as aerospace cables, heat-shrinkable sleeves for electronic appliances, architectural films, heating cables in chemical plants, oil field detection cables, satellite cables, and electric tools cables etc.
Product performance index:
Product 产品 | Density 密度g/cm3 | Melting point熔点 ℃ | 拉伸强度MPa | 断裂伸长率 % | Fluoride escape is 1ppm 氟化物逸出量1ppm | 加工温度 ℃ |
TS-4150LF | 1.75 | 260 | 35~45 | 15~250 | <40 | 260~320 |