UL20327
Hwatek
HT2103677
Product Description
| Construction | ||||
| Conductor | Tinned copper stranded | |||
| Cross section | 28AWG | |||
| Construction | 7/0.127mm | |||
| Strand Dia. | 0.38mm | |||
| Insulation | TPE | |||
| Nom.Thickness | 0.20mm | |||
| Min.Thickness | 0.18mm | |||
| Insulation Dia. | 0.80±0.05mm | |||
| Insulation colour | 1.black 2.brown 3.red 4.orange 5.yellow 6.green 7.blue | |||
| Filler | Optional | |||
| Material | Al-mylar(foil face out)，≥25% | |||
| Drain wire | Tinned copper stranded ，7/0.127mm | |||
| Assembly | 7C×28AWG+AE | |||
| Braid | Tinned copper，0.10mm，≥85% | |||
| Material | Paper，≥25% | |||
| Jacket | TPE | |||
| Nom.Thickness | 0.76mm | |||
| Min.Thickness | 0.61mm | |||
| Outer Dia. | 5.00±0.20mm | |||
| Colour | black | |||
| Mechanical Performance | ||||||
| Jacket | ||||||
| Material | TPE | |||||
| Tensile strength | ≥8.27MPa | |||||
| Elongation | ≥200% | |||||
| Aged condition | 136±1℃×168h | |||||
| Percent of original tensile strength | ≥75% | |||||
| Percent of original elongation | ≥75% | |||||
Product Description
| Construction | ||||
| Conductor | Tinned copper stranded | |||
| Cross section | 28AWG | |||
| Construction | 7/0.127mm | |||
| Strand Dia. | 0.38mm | |||
| Insulation | TPE | |||
| Nom.Thickness | 0.20mm | |||
| Min.Thickness | 0.18mm | |||
| Insulation Dia. | 0.80±0.05mm | |||
| Insulation colour | 1.black 2.brown 3.red 4.orange 5.yellow 6.green 7.blue | |||
| Filler | Optional | |||
| Material | Al-mylar(foil face out)，≥25% | |||
| Drain wire | Tinned copper stranded ，7/0.127mm | |||
| Assembly | 7C×28AWG+AE | |||
| Braid | Tinned copper，0.10mm，≥85% | |||
| Material | Paper，≥25% | |||
| Jacket | TPE | |||
| Nom.Thickness | 0.76mm | |||
| Min.Thickness | 0.61mm | |||
| Outer Dia. | 5.00±0.20mm | |||
| Colour | black | |||
| Mechanical Performance | ||||||
| Jacket | ||||||
| Material | TPE | |||||
| Tensile strength | ≥8.27MPa | |||||
| Elongation | ≥200% | |||||
| Aged condition | 136±1℃×168h | |||||
| Percent of original tensile strength | ≥75% | |||||
| Percent of original elongation | ≥75% | |||||