Product Introduction：
Foamed polyperfluoroethylene propylene (FEP) nucleating agent is used for FEP physical foaming cables, adding 5~10% can reach 45~55% foaming degree, easy to use and excellent performance. Mainly used in foamed FEP coaxial cables, foamed FEP high-speed transmission lines, critical CO2 FEP foamed materials and other fields
Performance indicators of foamed polyperfluoroethylene propylene nucleating agent：
测试项目Test project | 单位Unit | 数值NA | 试验条件 Test Condition |
密度Density | g/cm3 | 2.14 | GB/T2951.3-2008 |
硬度Hardness | 邵氏A | 95 | GBT 2411-2008 |
熔融指数Melt index | g/10min | 20 | 230℃/2.16kg |
拉伸强度 | MPa | 15 | ISO572-2 |
屈服伸长率 | % | 10 | ISO572-2 |
介电常数 1MHz | \ | 2.03 | GB 1693-1981 |
损耗因子1MHz | \ | 0.0006 | GB 1693-1981 |
| 1GHz | \ | 0.0004 | GB 1693-1981 |
体积电阻率 Volume Resistivity | Ω.m | 2 ×1016 | GB/T 1410-2006 |
氧指数Oxygen Index | % | 43 | GB/T2406-1993 |
熔融温度 | ℃ | 255 | ASTM D4591 |
Product Introduction：
Foamed polyperfluoroethylene propylene (FEP) nucleating agent is used for FEP physical foaming cables, adding 5~10% can reach 45~55% foaming degree, easy to use and excellent performance. Mainly used in foamed FEP coaxial cables, foamed FEP high-speed transmission lines, critical CO2 FEP foamed materials and other fields
Performance indicators of foamed polyperfluoroethylene propylene nucleating agent：
测试项目Test project | 单位Unit | 数值NA | 试验条件 Test Condition |
密度Density | g/cm3 | 2.14 | GB/T2951.3-2008 |
硬度Hardness | 邵氏A | 95 | GBT 2411-2008 |
熔融指数Melt index | g/10min | 20 | 230℃/2.16kg |
拉伸强度 | MPa | 15 | ISO572-2 |
屈服伸长率 | % | 10 | ISO572-2 |
介电常数 1MHz | \ | 2.03 | GB 1693-1981 |
损耗因子1MHz | \ | 0.0006 | GB 1693-1981 |
| 1GHz | \ | 0.0004 | GB 1693-1981 |
体积电阻率 Volume Resistivity | Ω.m | 2 ×1016 | GB/T 1410-2006 |
氧指数Oxygen Index | % | 43 | GB/T2406-1993 |
熔融温度 | ℃ | 255 | ASTM D4591 |